Our high-precision jewelry casting resin is engineered with 82% meltable wax content, offering performance that closely replicates traditional lost wax casting. Ideal for solid gauge designs, this advanced resin ensures clean burnout, no ash residue, and sharp, detailed results. With its wax-like behavior, it works seamlessly with standard investment materials, reducing thermal expansion and casting defects such as carbon buildup or swelling. Trusted by jewelers, it’s perfect for rings, earrings, pendants, and intricate custom designs. Designed for use with DLP and LCD printers.
Key features:
82% meltable wax content mimics traditional lost wax casting
Clean burnout with no ash residue
Compatible with standard investment materials
Reduces thermal expansion and casting defects
Ideal for rings, earrings, pendants, and custom designs
It is recommended to use a 37/100 water to powder ratio for investing large, thicker prints, and a 38/100 ratio for lighter, smaller prints. Using more water will create a weaker investment mold for burning out resin. After investing is completed, and before proceeding with burnout, allow invested flasks to sit (bench-set) undisturbed in a vibration-free area for a minimum of 3 to 4 hours (3 hours for flask sizes less than 3” x 4” (76.2 x 101.6 mm) and up to 4 hours for larger flask sizes). Drying out the investment and removing too much moisture can lead to mold cracks and metal flashing.
Specifications:
| Property | Value | Standard |
| Density: | 1.08 gram/cm3 | ASTM D1475-13(2020) |
| Tensile Strength: | 11 MPa | ASTM D638-14 |
| Flexural Strength: | 7.06 MPa | ASTM D790-02 |
| Flexural Modulus: | 170 MPa | ASTM D790-02 |
| Shore D Hardness: | 58 | ASTM D2240-15(2021) |
| Viscosity: | 9.53 Seconds | DIN 53211-4 |